| Acrylic ester polymers emulsion. |
| |
|
|
| |
|
|
| Appearance |
: |
Milky liquid of low viscosity |
| |
|
|
| Main ingredient |
: |
Copolymers of Acrylic Esters |
| |
|
|
| Ionic Nature |
: |
Non Ionic |
| |
|
|
| Stability |
: |
6 months |
| |
|
|
| pH |
: |
6.5 to 7 |
| |
|
|
| Solubility |
: |
Soluble in water. |
| |
|
|
|
| |
| |
|
|
A strong binding power is its main characteristic property. It is an excellent binder for Pigment Colour Printing Process. The Prints prepared from FINOBIND ALN and cylinder dried or stanter dried are perfectly wash fast. It also has excellent binding property for Khadi Printing Process. |
|
| |
| |
| FINOBIND ALN is applied not only for over Printing Process but also to discharge and resist Printing Process because it is compatible with Chemicals commonly used for this purpose |
| |
| |
: |
The above information is in good faith but without warranty. |
| |
|
|
|
| |
|
| |
|
|
|
| |
|
|
(Self Cross Linking acrylic Co-polymer Emulsion) |
| |
|
|
|
| |
|
|
| Appearance |
: |
Milky White Paste |
| |
|
|
| Ionic Nature |
: |
Non Ionic |
| |
|
|
| pH (1 to 5 % Solution) |
: |
6 - 8. |
| |
|
|
| RE-EMULSIFICATION |
: |
Excellent |
| |
|
|
| SOLUBILITY |
: |
Easily Soluble in water |
| |
|
|
|
| |
|
|
|
| |
|
|
FINOBIND 40 has a strong Binding Power. It produces a print of high rubbing and Washing Fastness. |
| |
|
|
|
| |
|
|
| Pigment |
X Gram |
| |
|
| Binder |
10 Parts |
| |
|
| Water |
10 Parts |
| |
|
| Kerosene |
80 Parts |
| |
|
| Fixer |
1 – 2 Parts |
| |
|
|
|
| |
|
|
PRINT – DRY – CURE at 1400C for 5 minutes . |
| |
|
|
|
| |
|
|
|
| |
: |
The above information is in good faith but without warranty. |
| |
|
|
|
| |
|
| |
|
|
|
FINOBIND 94 is a self, cross linking and self thickening Acrylic Emulsions having soft, durable film properties with excellent thermal and mechanical stability. FINOBIND 94 is used mainly in the field of textile flocking. |
| |
|
|
|
| |
|
|
| Appearance |
: |
Milky white liquid |
| |
|
|
| Chemical Nature |
: |
Acrylic Emulsions |
| |
|
|
| Emulsifying System |
: |
Anionic |
| |
|
|
| pH (when packed) |
: |
3 to 4 |
| |
|
|
| Storage |
: |
Protect from freezing |
| |
|
|
| Curing Temperature |
: |
1500C with catalyst PD |
| |
|
|
| Curing time |
: |
5 – 7 minutes |
|
| |
|
|
|
FINOBIND 94 being self cross linking acrylic emulsions catalyst is not needed to achieve durability to washing and dry cleaning. However, to increase the rate of cross linking under the normal conditions of curing catalyst PD is recommended. |
| |
|
|
|
| |
|
|
|
Suggested recipe for flockin |
| |
|
|
| FINOBIND 94 |
: |
80 – 90 parts |
| |
|
|
| Ammonia (20%) |
: |
4 – 6 parts |
| |
|
|
(to adjust pH 9 to 9.5) |
|
|
| Catalyst (25%) |
: |
4 part |
| |
|
|
| Fixer |
: |
1– 2 parts |
| |
|
|
| Glycerine /DEG |
: |
2 3 parts |
|
_______________ |
|
100 parts |
| |
|
|
|
Addition of water upto 5 parts may be made to adjust the finals viscosity. Fixer, Glycerine /DEG and Catalyst addition should preferable be made after adjusting pH 9 9.5 by Ammonia.
The material is coated, flocked, dried and cured in the normal way. |
| |
|
|
| |
: |
The above information is in good faith but without warranty. |
| |
|
|
|
| |
|
| |
|
|
|
| |
|
|
|
| |
|
|
|
| |
|
Appearance |
: |
White pourable viscous paste |
| |
|
|
| Ionic |
: |
Non Ionic |
| |
|
|
| pH |
: |
Neutral |
| |
|
|
Solubility |
: |
Soluble in cold as well as hot water |
| |
|
|
| Stability |
: |
Stable to hard water |
| |
|
|
| Shelf Life |
: |
Good |
| |
|
|
|
|
| |
|
|
FINOBIND GB is used for Printing Process Gold (Bronze) powder on Textile fabric. It gives excellent fastness and maintains brightness . |
| |
|
|
| |
|
|
RECIPE FOR EMULSION THICKENING |
| |
|
|
| 18 |
Parts |
Water |
| 2 |
Parts |
Emulsifier |
| 80 |
Parts |
Kerosene |
____ |
|
____ |
|
|
|
| |
|
|
|
| |
|
|
| 150 – 180 |
Parts |
Water |
| 320 |
Parts |
Emulsifier |
| 20 |
Parts |
Kerosene |
| Balance |
Parts |
EMULSION THICKENER |
_________________ |
|
_________________ |
|
|
|
| |
|
|
 |
Emulsifier should be added only in case of choking problems |
| |
|
|
Fixer should be added while Printing Process only. |
| |
|
|
Do not add Catalyst DAP , Catalyst LCP , Urea, Kerosene etc |
| |
|
|
If higher tackiness is observed ½ to 1% DEG can be added |
| |
|
|
Containers must be kept closed while Printing Process and after use to avoid drying of the materials and skein formation. |
| |
|
|
Coconut oil can be applied at the back of the screen to avoid sticking of the material with screen. |
| |
|
|
Print with 100 – 200 mesh screen, dry and cure at 1500C for 3 – 5 minutes. |
| |
|
|
| |
: |
The above information is in good faith but without warranty. |
|
|
| |
| |
| |
|
|
| |
| |
|
|
| |
| |
|
| |
|
|
|
Appearance
|
: |
White pourable viscous paste |
| |
|
|
| Ionic |
: |
Non Ionic |
| |
|
|
| pH |
: |
Neutral |
| |
|
|
Solubility |
: |
Soluble in cold as well as hot water |
| |
|
|
| Stability |
: |
Stable to hard water |
| |
|
|
| Shelf Life |
: |
Good |
| |
|
|
|
|
| |
FINOBIND JR is used for Printing Process Jari (Glitter) powder on Textile fabric. It gives excellent fastness and maintains brightness. |
| |
|
|
| |
| |
|
|
RECIPE FOR EMULSION THICKENING: |
| |
|
|
| 18 |
Parts |
Water |
| 2 |
Parts |
Emulsifier |
| 80 |
Parts |
Kerosene |
____ |
|
____ |
|
|
|
| |
|
|
|
| |
|
|
| 150 – 180 |
Parts |
Gold (Bronze) powder |
| 320 |
Parts |
FINOBIND JR |
| 20 |
Parts |
FINOFIX CL |
| Balance |
Parts |
EMULSION THICKENER |
_________________ |
|
_________________ |
|
|
|
| |
|
|
|
Emulsifier should be added only in case of choking problems |
| |
|
|
Fixer should be added while Printing Process only. |
| |
|
|
Do not add Catalyst DAP , Catalyst LCP , Urea, Kerosene etc |
| |
|
|
If higher tackiness is observed ½ to 1% DEG can be added |
| |
|
|
Containers must be kept closed while Printing Process and after use to avoid drying of the materials and skein formation. |
| |
|
|
Coconut oil can be applied at the back of the screen to avoid sticking of the material with screen. |
| |
|
|
Print through 100 – 200 mesh screen, dry and cure at 1500C for 3 – 5 minutes. |
| |
| |
: |
The above information is in good faith but without warranty. |
|
| |
|
|
| APEO free acrylate based pigment printing binder for Direct, Discharge and Resist printing. |
| |
|
|
| |
|
|
|
| |
|
|
| Nature |
: |
APEO free aqueous dispersion of a thermally cross
linkable acrylate co polymer. |
| |
|
|
| Appearance |
: |
Slightly viscous liquid. |
| |
|
|
| Ionic Nature |
: |
Non ionic |
| |
|
|
| pH |
: |
7 8 |
| |
|
|
| Storage |
: |
Miscible with water in all proportions |
| |
|
|
| Shelf life |
: |
At least 12 months.
Once the drum has been opened, the product should be used up as soon as possible. After the product has been taken out the drum must be properly resealed as the binder tends to form a skin upon explosure to air. |
| |
|
|
|
|
| |
|
|
| Direct Printing |
: |
Coloured print, matt-white, and matt-coloured prints on white and dyed materials, flock printing, gold & bronze printing. |
| |
|
|
| Resist Printing |
: |
Suitable |
| |
|
|
| Discharge Printing |
: |
Suitable |
| |
|
|
| Guideline Receipe |
: |
x gms water
80 150g FINOBIND AQBD
2 3g Rheological modifier
10 12g Acrylic thickner
1000 gms. |
| |
|
|
| FIXATION: |
|
|
| |
|
|
| Polymerser |
: |
4 5 min at 1500C or
3 4 min at 160 -1700C |
| |
|
|
| Loop Steamer |
: |
5 7 min at 1600C |
| |
|
|
|
| |
|
|
| |
: |
The above information is in good faith but without warranty. |
|
FINOBIND –ALN